型号:SE1GFN3-701
材料特性:玻纤增强
应用领域:医疗护理
联系电话:
联系手机:13061954669
联系人:蒋先生
让卖家联系我
详细介绍
PPO基础创新塑料(美国)物性表
比重 | 1.31 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.1~0.4 % | Internal | flow, 3.2 mm |
吸水率 | 0.06 % | ASTM D570 | 24 hours |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 5 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 172 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
弯曲模量 | 7790 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 96 J/m | ASTM D256 | |
23℃ (73℉) | 117 J/m | ASTM D256 | |
洛氏硬度L | 108 L | ASTM D 785 | |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 140 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 135 °C | ASTM D648 | 6.4 mm, unannealed |
相对温度指数(RTI) | |||
冲击w/impact,- | 105 °C | UL 746B | |
电气Elec,- | 110 °C | UL 746B | |
强度w/o impact,- | 110 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25.2 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
UL 防火等级 | |||
V-1 | 1.47 mm | UL94 | |
V-0 | 5.99 mm | UL94 | |
氧指数(LOI) | 35.5 % | ISO 4589 |
聚苯醚PPO结构式
这是美国在1966年开始工业化生产,原料为苯酚和甲醛,先合成2,6二甲某酚,然后科进行气化、偶合反应,制得聚苯醚的单体,再缩聚、精制,即得白色粉
末状的聚合物,其分子量在6万 9 17万之间,比重1.07。