PA12基础创新塑料(美国)供应商 (PA12基础创新塑料(美国)SP003) 现货供应
![](http://img2.11467.com/2023/12-21/1327918771.jpg)
![](http://static.11467.com/img/ab-prev-0.png)
![](http://img2.11467.com/2023/12-21/1327918771_small.jpg)
![](http://img2.11467.com/2023/12-21/1327078899_small.jpg)
![](http://img.11467.com/2023/12-21/1324642161_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-06-28 07:00:00
价格:请来电询价
型号:SP003
代理商:基础创新塑料美国一级代理
材料特性:润滑耐磨
联系电话:
联系手机:13061954669
联系人:蒋先生
让卖家联系我
详细介绍
物性表
PA12基础创新塑料(美国)SP003
收缩率 | MD:24小时 | ASTMD955 | 0.90to1.1 | % |
收缩率 | TD:24hr | ASTMD955 | 1.8to2.0 | % |
收缩率 | TD:24小时 | ISO294-4 | 1.9 | % |
收缩率 | MD:24小时 | ISO294-4 | 1.0 | % |
吸水率 | 24hr,50%RH | ASTMD570 | 0.20 | % |
拉伸模量2 | ASTMD638 | 1380 | Mpa | |
拉伸模量 | ISO527-2/1 | 1580 | Mpa | |
抗张强度 | 屈服 | ASTMD638 | 37.9 | Mpa |
摩擦系数 | Dynamic | ASTMD3702Modified | 0.23 | |
摩擦系数 | Static | ASTMD3702Modified | 0.14 | |
磨损因数-Washer | ASTMD3702Modified | 13.5 | 10^-10in^5-min/ft-lb-hr | |
拉伸应力 | 屈服 | ISO527-2 | 38.0 | Mpa |
抗张强度 | 断裂 | ASTMD638 | 35.2 | Mpa |
拉伸应力 | 断裂 | ISO527-2 | 36.0 | Mpa |
伸长率 | 屈服 | ASTMD638 | 18 | % |
拉伸应变 | 屈服 | ISO527-2 | 18 | % |
伸长率 | 断裂 | ASTMD638 | 24 | % |
拉伸应变 | 断裂 | ISO527-2 | 33 | % |
弯曲模量 | ASTMD790 | 1380 | Mpa | |
弯曲模量 | ISO178 | 1300 | Mpa | |
弯曲应力 | ISO178 | 44.0 | Mpa |
热变形温度4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 134 | °C |
热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 146 | °C |
热变形温度4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 147 | °C |
线形热膨胀系数 | MD:-40到40°C | ASTME831 | 1.1E-04 | cm/cm/°C |
线形热膨胀系数 | MD:-40到40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
线形热膨胀系数 | TD:-40到40°C | ASTME831 | 1.1E-04 | cm/cm/°C |
线形热膨胀系数 | TD:-40到40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 150 | °C |
PA12(聚合酰胺12)
良好的耐化学性:PA12具有良好的化学稳定性,耐酸 碱、耐油脂、耐有机溶剂等。