TPU3385A耐磨级
密度 | ASTM D792/ISO 2781/JIS K7311 | 1200 | ||
硬度 A | ASTM D2240/ISO 868 | 85 | Shore A | |
硬度 D | ASTM D2240/ISO 868 | 33 | Shore D | |
回弹性 | ASTM D2630/ISO 4662 | 50 | % | |
模量 | ASTM D412/ISO 527 | 5 | Mpa/Psi | |
300%模量 | ASTM D412/ISO 527 | 15 | Mpa/Psi | |
抗张强度 | ASTM D412/ISO 527 | 50 | Mpa/Psi | |
撕裂强度 | ASTM D624/ISO 34 | 70 | n/mm² | |
磨耗损失 | ISO 4649 | 25 | mm³ | |
弯曲模量 | ASTM D790/ISO 178 | 17 | Mpa/Psi | |
压缩变形率 | ISO 815 | 42 | % | |
ISO 815 | 15 | % | ||
模具温度 | 20 | °C | ||
熔体温度 | 190~210 | °C |
硬段含量
硬段含量是指硬段在中的质量百分数,是配方设计中一个重要参数。硬段含量直接影响的氢键、微相分离程度以及结晶性能, 是决定其形态的主要因素。一般来讲, 随着硬段含量的增加,TPU的硬度、模量以及撕裂强度等增加, 而扯断伸长率下降。
异氰酸酯指数
由于TPU的合成机理是在官能团之间进行的逐步加聚反应, 所以异氰酸酯指数r0(二异氰酸酯与低聚物二醇的摩尔比) 直接影响分子量的大小。r0≤1时,TPU分子量随着r0的增大而增大,当r0=1时,分子量达到大, 再继续增加r0值,分子量又开始下降。r0在0.95~1之间时,TPU模量、拉伸强度、撕裂强度等随着r0的增加而增加。
TPU按分子结构来分类可分为:聚酯型和聚醚型两种;
按照加工方式的分类又可分为:注塑级、吹塑级、挤出级、脱模级、吹膜级、发泡级、涂覆级、中空级、滚塑级、拉丝级、热熔级等等;