PPO基础创新塑料(美国)N190X-71283物性表物理性能值/单位测试标准测试条件比重1.13 -ASTM D792熔体体积流动速率(MVR)


280°C/5.0 kg23 cm³/10 minISO 1133熔体质量流动速率(MFR)


250°C/10.0 kg19.3 g/10 minASTM D 1238收缩率


纵向(Flow)0.5~0.7 %Internalflow, 3.2 mm吸水率0.08 %ASTM D570磨耗76 mg/1000cyASTM D 1044CS-17, 1 kg机械性能值/单位测试标准测试条件拉伸强度


屈服(yld)60 MpaASTM D638Type I, 50 mm/min屈服(yld)58 MpaISO 52750 mm/min断裂(brk)50 MpaISO 52750 mm/min断裂(brk)47 MpaASTM D638Type I, 50 mm/min拉伸延伸率


屈服(yld)3.6 %ASTM D638Type I, 50 mm/min屈服(yld)3.2 %ISO 52750 mm/min断裂(brk)9 %ASTM D638Type I, 50 mm/min断裂(brk)9.2 %ISO 52750 mm/min弯曲强度


屈服(yld)98 MpaASTM D7901.3 mm/min, 50 mm span屈服(yld)91 MpaASTM D7902.6 mm/min, 100 mm span屈服(yld)87 MpaISO 1782 mm/min弯曲模量2500 MpaASTM D7901.3 mm/min, 50 mm span弯曲模量2300 MpaASTM D7902.6 mm/min, 100 mm span弯曲模量2350 MpaISO 1782 mm/min拉伸模量2580 MpaASTM D63850 mm/min拉伸模量2600 MpaISO 5271 mm/min冲击性能值/单位测试标准测试条件简支梁缺口(Charpy Notched)


23℃ (73℉)20 kJ/m²ISO 179/2C悬臂梁缺口(Izod Notched)


23℃ (73℉)293 J/mASTM D25623℃ (73℉)20 kJ/m²ISO 180/1A80*10*4悬臂梁无缺口(Izod Unnotched)


-30℃ (-22℉)100 J/mASTM D 481223℃ (73℉)720 J/mASTM D4812仪器化落镖冲击能量


23℃ (73℉)峰值50 JASTM D3763硬度性能值/单位测试标准测试条件洛氏硬度R120 RASTM D785热学性能值/单位测试标准测试条件热变形温度(HDT)


0.45 Mpa (66 psi)（4.6kg/cm²）95 °CASTM D6483.2mm, unannealed0.45 Mpa (66 psi)（4.6kg/cm²）95 °CISO 75/BeEdgew 120*10*4 sp=100mm1.8 Mpa (264 psi)（18.6kg/cm²）78 °CASTM D6483.2mm, unannealed1.8 Mpa (264 psi)（18.6kg/cm²）86 °CASTM D6486.4 mm, unannealed1.8 Mpa (264 psi)（18.6kg/cm²）82 °CISO 75/AeEdgew 120*10*4 sp=100mm维卡软化温度(Vicat)104 °CASTM D1525Rate B/50维卡软化温度(Vicat)107 °CISO 306Rate B/120相对温度指数(RTI)


冲击w/impact,-80 °CUL 746B电气Elec,-95 °CUL 746B强度w/o impact,-95 °CUL 746B线性膨胀系数(CLTE)


纵向(Flow)77 E-6/°CASTM E831-40°C to 40°C, flow横向(Across Flow)81 E-6/°CASTM E831-40°C to 40°C, xflow导热系数0.24 W/m-°CASTM C 177燃烧性能值/单位测试标准测试条件UL 防火等级


HB1 mmUL94Min.V-01.5 mmUL94Min.5VA3 mmUL94Min.氧指数(LOI)39 %ASTM D 2863灼热丝可燃性指数(GWFI)


1mm960 °CIEC 60695-2-122mm960 °CIEC 60695-2-123mm960 °CIEC 60695-2-12灼热丝点燃温度(GWIT)


1.0mm800 °CIEC 60695-2-132.0mm775 °CIEC 60695-2-133.0mm775 °CIEC 60695-2-13紫外线暴露,水暴露试验和浸渍F1 -UL 746C

PPO电子电器应用

PPO可用作5G基站移相器介质块，改变电磁波的相位差，获得目标信号，实现5G互联。

PPO水处理相关行业应用

由于耐水解和优良的尺寸稳定性，在水处理方面应用，如水泵壳体、外壳、过流部件等。