PPO基础创新塑料(美国)N190X-111 PPO基础创新塑料(美国)授权代理
PPO基础创新塑料(美国)N190X-111物性表
| 比重 | 1.13 - | ASTM D792 | |
| 熔体体积流动速率(MVR) | |||
| 280°C/5.0 kg | 23 cm³/10 min | ISO 1133 | |
| 熔体质量流动速率(MFR) | |||
| 250°C/10.0 kg | 19.3 g/10 min | ASTM D 1238 | |
| 收缩率 | |||
| 纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
| 吸水率 | 0.08 % | ASTM D570 | |
| 磨耗 | 76 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| 拉伸强度 | |||
| 屈服(yld) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
| 屈服(yld) | 58 Mpa | ISO 527 | 50 mm/min |
| 断裂(brk) | 50 Mpa | ISO 527 | 50 mm/min |
| 断裂(brk) | 47 Mpa | ASTM D638 | Type I, 50 mm/min |
| 拉伸延伸率 | |||
| 屈服(yld) | 3.6 % | ASTM D638 | Type I, 50 mm/min |
| 屈服(yld) | 3.2 % | ISO 527 | 50 mm/min |
| 断裂(brk) | 9 % | ASTM D638 | Type I, 50 mm/min |
| 断裂(brk) | 9.2 % | ISO 527 | 50 mm/min |
| 弯曲强度 | |||
| 屈服(yld) | 98 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 屈服(yld) | 91 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| 屈服(yld) | 87 Mpa | ISO 178 | 2 mm/min |
| 弯曲模量 | 2500 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 弯曲模量 | 2300 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| 弯曲模量 | 2350 Mpa | ISO 178 | 2 mm/min |
| 拉伸模量 | 2580 Mpa | ASTM D638 | 50 mm/min |
| 拉伸模量 | 2600 Mpa | ISO 527 | 1 mm/min |
| 简支梁缺口(Charpy Notched) | |||
| 23℃ (73℉) | 20 kJ/m² | ISO 179/2C | |
| 悬臂梁缺口(Izod Notched) | |||
| 23℃ (73℉) | 293 J/m | ASTM D256 | |
| 23℃ (73℉) | 20 kJ/m² | ISO 180/1A | 80*10*4 |
| 悬臂梁无缺口(Izod Unnotched) | |||
| -30℃ (-22℉) | 100 J/m | ASTM D 4812 | |
| 23℃ (73℉) | 720 J/m | ASTM D4812 | |
| 仪器化落镖冲击能量 | |||
| 23℃ (73℉)峰值 | 50 J | ASTM D3763 | |
| 洛氏硬度R | 120 R | ASTM D785 | |
| 热变形温度(HDT) | |||
| 0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ASTM D648 | 3.2mm, unannealed |
| 0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
| 1.8 Mpa (264 psi)（18.6kg/cm²） | 78 °C | ASTM D648 | 3.2mm, unannealed |
| 1.8 Mpa (264 psi)（18.6kg/cm²） | 86 °C | ASTM D648 | 6.4 mm, |