大陆现货TPU德国巴斯夫1195A10(副牌)
物性表TPU德国巴斯夫1195A10
熔体质量流动速率 | 210°C/10.0kg | ASTMD1238 | 35to65 | g/10min |
拉伸模量 | 注塑 | ASTMD412 | 51.7 | Mpa |
弯曲模量 | 注塑 | ASTMD790 | 52.4 | Mpa |
泰伯耐磨性 | ASTMD1044 | 55.0 | mg | |
Abrasion-DIN | DIN53516 | 25 | mm³ | |
断裂拉伸强度 | ASTM D-412 | 48.3 | Mpa | |
伸长率 | 断裂 | ASTM D-412 | 450 | % |
撕裂强度 | ASTM D-624 | 140 | kN/m | |
硬度 | shoreA | ASTM D-648 | 95 | |
拉伸模量 | ASTM D-638 | 41.4 | Mpa | |
100%拉伸应力 | ASTM D-412 | 16.5 | Mpa | |
维卡软化点 | ASTM D-1525 | 116 | °C | |
玻璃转化温度 | 内部方法 | -28.0 | °C | |
维卡软化温度 | ASTMD1525 | 127 | °C | |
SofteningPoint-DMA | 内部方法 | 89 | °C | |
伸长率 | 断裂 | ASTMD412 | 430 | % |
撕裂强度2 | ASTMD624 | 140 | kN/m | |
压缩变形 | 23°C,22hr | ASTMD395B | 30 | % |
70°C,22hr | ASTMD395B | 45 | % | |
拉伸应力 | 应变 | ASTMD412 | 17.2 | Mpa |
300%应变 | ASTMD412 | 35.9 | Mpa | |
抗张强度 | ASTMD412 | 39.3 | Mpa | |
肖氏硬度 | 邵氏A | ASTMD2240 | 95 | |
UL阻燃等级 | 0.75mm | UL94 | HB | |
3.0mm | UL94 | HB | ||
密度 | ASTM D-792 | 1.14 | g/cm | |
熔融指数 | ASTM D-1238 | 50 | g/10min |