美国伊斯曼PCTGFX200 不含双酚A耐化学原料
美国伊斯曼PCTGFX200物性表
吸水率 | 23°C,24hr,0.254mm | ASTMD570 | 0.50 | % |
TaberAbrasionResistance2 | 23°C,250.0µm | ASTMD1044 | 20Haze | % |
比热 | 60°C | DSC | 1700 | J/kg/°C |
100°C | DSC | 1900 | J/kg/°C | |
150°C | DSC | 2300 | J/kg/°C | |
200°C | DSC | 2400 | J/kg/°C | |
250°C | DSC | 2600 | J/kg/°C | |
熔融温度 | 119 | °C | ||
线形热膨胀系数 | MD:23°C | ASTMD696 | 8E-05 | cm/cm/°C |
开裂6 | ASTMD1938 | 9.0 | kN/m | |
开裂7 | ASTMD1938 | 10 | kN/m | |
落锤冲击4 | -30°C,250µm | ASTMD1709A | 830 | g |
-18°C,250µm | ASTMD1709A | 830 | g | |
23°C,250µm | ASTMD1709A | 830 | g | |
裤型撕裂耐性5 | MD:250µm | ISO6383-1 | 10.0 | N/mm |
TD:250µm | ISO6383-1 | 9.00 | N/mm | |
透氧率 | 23°C,250µm,50%RH | ASTMD3985 | 44 | cm³·mm/m²/atm/24hr |
水气透过率 | 23°C,RH,250µm | ASTMF1249 | 4.0 | g/m²/24hr |
38°C,RH,250µm | ASTMF1249 | 10 | g/m²/24hr | |
CarbonDioxidePermeability | 23°C,254.0µm | ASTMD1434 | 210 | cm³·mm/m²/atm/24hr |
埃尔曼多夫抗撕强度 | MD:23°C,250.0µm | ASTMD1922 | 4 | N |
薄膜厚度-经测试 | 250 | µm | ||
膜刺穿强度3 | 250µm | ASTMD3763 | 4.50 | J |
割线模量-MD | 250µm | ASTMD882 | 1500 | Mpa |
割线模量-TD | 250µm | ASTMD882 | 1400 | Mpa |
抗张强度-MD | 屈服,250µm | ASTMD882 | 43.0 | Mpa |
拉伸强度-TD | Yield,250µm | ASTMD882 | 41.0 | Mpa |
拉伸强度-MD | Break,250µm | ASTMD882 | 57.0 | Mpa |
拉伸强度-TD | Break,250µm | ASTMD882 | 42.0 | Mpa |
拉伸应变-MD | Yield,250µm | ASTMD882 | 8.0 | % |
拉伸应变-TD | Yield,250µm | ASTMD882 | 8.0 | % |
伸长率-MD | 断裂,250µm | ASTMD882 | 110 | % |
拉伸应变-TD | Break,250µm | ASTMD882 | 120 | % |
埃尔曼多夫抗撕强度 | TD:23°C,250.0µm | ASTMD1922 | 4 | N |
PPTTearResistance | MD:23°C,250.0µm | - | 40 | N |
TD:23°C,250.0µm | - | 40 | N | |
抗撕裂蔓延性 | MD:23°C,250.0µm | ASTMD1938 | 310 | gf |
TD:23°C,250.0µm | ASTMD1938 | 200 | gf |
PCTG产品简介 :PET树脂是由二元醇(乙二醇,EG)与二元酸(对苯二甲酸,TPA)缩聚而成线型均聚聚酯,而共聚聚酯是用醇或酸改性的聚酯,有PETG、PCTG和PCTA以及可降解的共聚聚酯。